Markforged – Desktop Series

3D Printers - The Markforged Desktop Series combines industrial quality and affordability in an all-aluminum form factor that fits on your desktop.

Onyx One 3d Printer

Process: Fused Filament Fabrication
Build Volume: 320 x 132 x 154 mm
Layer Height:100um default, 200um maximum
Ultimate Tensile Strength: UTS: 36 MPa (1.2x ABS)
Flex Stifness: 2.9 GPa (1.4x ABS)
Plastics Available: Onyx (800cm3 included)
Fibers Available: None
Supplied Software: Markforged Software

Shipping – Collect from CADPRO System, Auckland

Onyx Pro 3d Printer

Process: Continuous Fibre Reinforced Plastics
Build Volume: 320 x 132 x 154 mm
Layer Height:100um default, 200um maximum
Ultimate Tensile Strength: 590 MPa (19.0x ABS, 16.4x Onyx)
Max Flexural Stifness: 22 GPa (10.7x ABS, 7.6x Onyx)
Plastics Available: Onyx (800cm3 included)
Fibers Available: Fibreglass (50cm3 included)
Supplied Software: Markforged Software

Shipping – Collect from CADPRO System, Auckland

Mark Two 3d Printer Onyx

Process: Continuous Fibre Reinforced Plastics
Build Volume: 320 x 132 x 154 mm
Layer Height:100um default, 200um maximum
Ultimate Tensile Strength: 700 MPa (22.6x ABS, 19.4x Onyx)
Max Flexural Stifness: 51 GPa (24.8x ABS, 17.6x Onyx)
Plastics Available: Onyx (800cm3 included)
Fibers Available: Carbon Fiber, Fibreglass, Kevlar, High Strength/High Temp Fiberglass (50cm3 of each included)
Supplied Software: Markforged Software

Shipping – Collect from CADPRO System, Auckland

Mark Two 3d Printer Nylon

Process: Continuous Fibre Reinforced Plastics
Build Volume: 320 x 132 x 154 mm
Layer Height:100um default, 200um maximum
Ultimate Tensile Strength: 700 MPa (22.6x ABS, 19.4x Onyx)
Max Flexural Stifness: 51 GPa (24.8x ABS, 17.6x Onyx)
Plastics Available: Nylon (800cm3 included)
Fibers Available: Carbon Fiber, Fibreglass, Kevlar, High Strength/High Temp Fiberglass (50cm3 of each included)
Supplied Software: Markforged Software

Shipping – Collect from CADPRO System, Auckland

Total

Success Plan
Qty

Product Details

About This Product